Phosphorus oxide and phosphoric acid production processes

ABSTRACT

The present invention is generally directed to improved processes for the preparation of various phosphorus oxides and phosphoric acid. Phosphorus oxides prepared in accordance with the present invention include phosphorus (III) oxides (e.g., tetraphosphorus hexaoxide (P4O6)). Phosphorus (III) oxides such as P4O6 are useful products and are also useful as precursors in preparation of other products, including phosphorous acid (H3PO3) and other phosphorus-containing chemicals. Certain aspects of this invention are also directed to using various byproducts formed during P4O6 production as precursors for the formation of phosphoric acid (H3PO4) and P2O5. In particular, the present invention is directed to improved processes for the preparation of phosphorus (III) oxides (e.g., P4O6) suitable for use in the preparation of phospho-herbicides such N-(phosphonomethyl)glycine (glyphosate) and precursors thereof (e.g., N-(phosphonomethyl)iminodiacetic acid (PMIDA)). The present invention is thus further directed to preparation of these compounds.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Nonprovisional patent application Ser. No. 16/668,159, filed Nov. 19, 2019, which claims the benefit of U.S. Provisional Patent Application No. 62/769,252, filed Nov. 19, 2018, the entire contents of which are incorporated herein by reference.

FIELD OF THE INVENTION

The present invention is generally directed to improved processes for the preparation of various phosphorus oxides and phosphoric acid. Phosphorus oxides prepared in accordance with the present invention include phosphorus (III) oxides (e.g., tetraphosphorus hexaoxide (P₄O₆ )). Phosphorus (III) oxides such as P₄O₆ are useful products and are also useful as precursors in preparation of other products, including phosphorous acid (H₃PO₃) and other phosphorus-containing chemicals. Certain aspects of this invention are also directed to using various byproducts formed during P₄O₆ production as precursors for the formation of phosphoric acid (H₃PO₄) and P₂O₅. In particular, the present invention is directed to improved processes for the preparation of phosphorus (III) oxides (e.g., P₄O₆) suitable for use in the preparation of phospho-herbicides such N-(phosphonomethyl)glycine (glyphosate) and precursors thereof (e.g., N-(phosphonomethyl)iminodiacetic acid (PMIDA)). The present invention is thus further directed to preparation of these compounds.

BACKGROUND OF THE INVENTION

Methods for producing phosphorus (III) oxides such as P₄O₆ are known in the art. The term “P₄O₆” as used herein is intended to include all formulae conventionally used to define phosphorus (III) oxides, including P₂O₃. As used herein, the terms phosphorus (III) oxide and P₄O₆ are used interchangeably.

P₄O₆ is useful as a product itself and as a precursor for production of various other products. Methods to prepare P₄O₆ are known in the art and have proven to some extent to be effective, but there exists room for improvement in terms of yield, purity, and process efficiencies. For example, prior methods for producing P₄O₆ typically encounter limitations or issues during scale-up to commercial scale operations.

Both as a product itself and precursor for preparation of other compounds, P₄O₆ is often considered in comparison to phosphorus trichloride (PCl₃), which is conventionally used in various processes as a source of phosphorus. As a product itself, P₄O₆ if produced effectively on a commercial scale would provide an advantage over PCl₃ since it would contain a higher weight percent of phosphorus as compared to PCl₃ (over 50 weight % as compared to 22 weight %). P₄O₆ as a product itself would therefore provide a more concentrated phosphorus product and would avoid the issues and risks associated with the dangerous chemical chlorine required for production of PCl₃ and released as a byproduct of its production. These same advantages are provided when P₄O₆ is used as an alternative to PCl₃ as a precursor for preparing other compounds where, in one form or another (e.g., as hydrochloric acid) large amounts of chlorine are generated as undesired byproducts that must dealt with or disposed. In addition, intermediates and end products to be made from PCl₃ usually do not contain chloride. An alternative to PCl₃ as a starting material is phosphorous acid. However, phosphorous acid is generally prepared from PCl₃ and therefore does not completely avoid the undesired byproduct issue, but simply shifts it to another point in the process.

A need exists, therefore, for improved processes to prepare P₄O₆ as a phosphorus-containing product itself and as alternative to PCl₃ as a source of phosphorus for use in preparation of various phosphorus-containing compounds.

BRIEF SUMMARY OF THE INVENTION

Briefly, therefore, the present invention is directed to processes for the manufacture of phosphorus (III) oxide.

In various embodiments, the process comprises, in a reactor unit, reacting phosphorus with oxygen, thereby forming an intermediate reaction product stream comprising P₂O₃ and one or more byproducts; in a quenching unit, quenching the intermediate reaction product stream by contacting with a quenching liquid, thereby forming a reaction product slurry comprising P₄O₆ and one or more byproducts; recovering the one or more byproducts from the reaction product slurry; and in a vaporizer unit, vaporizing the one or more byproducts to form a vaporized recycle stream.

In other embodiments, the process comprises, in a reactor unit, reacting phosphorus with oxygen, thereby forming an intermediate reaction product stream comprising P₂O₃ and one or more byproducts; in a quenching unit, quenching the intermediate reaction product stream by contacting with a quenching liquid, thereby forming a reaction product slurry comprising liquid P₄O₆ and one or more byproducts; separating solid components of the reaction product slurry therefrom, thereby forming a slurry byproduct stream comprising the one or more solid byproducts and a crude product stream comprising liquid P₄O₆; and introducing at least a portion of the slurry byproduct stream into a vaporizer unit.

In still further embodiments of processes for the manufacture of phosphorus (III) oxide, the process comprises, in a reactor unit, reacting phosphorus with oxygen, thereby forming an intermediate reaction product stream comprising P₂O₃ and one or more byproducts; in a quenching unit, quenching the intermediate reaction product stream by contacting with a quenching liquid, thereby forming a reaction product slurry comprising liquid P₄O₆ and one or more solid byproducts; recovering the one or more solid byproducts from the reaction product slurry; and introducing the one or more solid byproducts into the reactor unit for direct cooling of the contents of the reactor unit, and wherein the temperature within the reactor unit is controlled by external cooling of the reactor unit.

The present invention is also directed to processes for the manufacture of phosphoric acid (H₃PO₄).

In certain such embodiments the process comprises reacting phosphorus with oxygen in a reactor unit, thereby forming an intermediate reaction product comprising P₂O₃ and one or more byproducts; in a quenching unit, quenching the intermediate reaction product by contacting with a quenching liquid, thereby forming a reaction product slurry comprising liquid P₄O₆ and one or more byproducts; separating the reaction product slurry into a crude liquid P₄O₆ stream and a thickened product slurry; introducing the crude liquid P₄O₆ stream into the quenching unit; separating liquid P₄O₆ from the thickened product slurry, thereby forming a crude product stream comprising liquid P₄O₆ and a byproduct stream comprising phosphorus (III), phosphorus (V) and/or phosphorus (III and V) oxides; introducing the byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the byproduct stream to produce a vapor product stream comprising P₂O₅ and/or P₄O₁₀; and contacting the vapor product stream with water, thereby forming a liquid product stream comprising H₃PO₄.

The present invention is also directed to processes for the manufacture of phosphorus pentoxide (P₂O₅).

In certain such embodiments, the process comprises reacting phosphorus with oxygen in a reactor unit, thereby forming an intermediate reaction product comprising P₂O₃ and one or more byproducts; in a quenching unit, quenching the intermediate reaction product by contacting with a quenching liquid, thereby forming a reaction product slurry comprising liquid P₄O₆ and one or more byproducts; separating liquid P₄O₆ from the reaction product slurry, thereby forming a crude product stream comprising liquid P₄O₆ and a byproduct stream comprising phosphorus (III), phosphorus (V) and phosphorus (III and V) oxides; introducing the byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the byproduct stream to produce a vapor product stream comprising P₄O₁₀; and condensing the vapor product stream, thereby forming a liquid product stream comprising P₂O₅.

The present invention is further directed to processes combining the embodiments listed above. For example, any of the embodiments describing processes for the preparation of phosphorus (III) oxide may be combined with the processes for the manufacture of phosphoric acid (H₃PO₄) and/or phosphorus pentoxide (P₂O₅) described above and/or elsewhere herein.

Other objects and features will be in part apparent and in part pointed out hereinafter.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 describes a schematic for a process/processes conducted in accordance with the present invention.

FIG. 2 describes a schematic for a process conducted in accordance with the present invention.

FIG. 3 describes a schematic for a process conducted in accordance with the present invention.

FIG. 4 describes a schematic for a process/processes conducted in accordance with the present invention.

FIG. 5 depicts the thermodynamic equilibrium of a phosphorus-oxygen (P—O) system for a molar ratio of P₄:O₂ of 1:3 using software modeling (HSC—http://www.hsc-chemistry.com).

Corresponding reference characters indicate corresponding parts throughout the drawings.

DETAILED DESCRIPTION OF THE INVENTION

The present invention includes improved processes for the production of P₄O₆. Improvements embodied in the methods of the present invention include: (i) the suitability of the methods of the present invention for operation on a commercial scale, (ii) improvements in yield, purity, and/or by-product profile for the P₄O₆ produced by the methods of the present invention, and (iii) methods for preparation of products using P₄O₆ as a precursor that avoid issues associated with other phosphorus-containing precursors (e.g., issues associated with PCl₃ due to the use and presence of chlorine).

The processes of the present invention include a combustion step where phosphorus (P₄) is reacted with an oxygen-containing gas (typically O₂) in a reactor to provide an intermediate product including P₂O₃ and one or more byproducts. The P₂O₃ is converted to P₄O₆ by contact with a quenching liquid in a quenching step. The product of the quenching step includes liquid P₄O₆ as a product along with various byproducts, including solid products and also various byproducts dissolved in the liquid phase. The present invention also includes recovery of the P₄O₆ from the product of the quenching unit, purification of the P₄O₆, and/or use of byproducts of P₄O₆ formation in the preparation of another product (e.g., phosphoric acid or phosphorus pentoxide).

Processes of the present invention also may include recovery of a byproduct stream from the P₄O₆-containing product of the quenching unit. In one aspect of the present invention, a solid byproduct stream is recovered and returned to the reactor unit. In various other aspects of the present invention, recovery of a byproduct stream (e.g., a mostly solid byproduct stream, or slurry byproduct stream) is followed by vaporization to provide a vaporized recycle stream. Vaporization is conducted in a unit specifically designed therefor and separate from the reactor unit. The vaporized recycled stream is introduced into the reactor as all or a portion of the source of phosphorus for the combustion step.

Overall, recovery of a byproduct stream from the product of the quenching unit improves process efficiencies by recovering phosphorus-containing species that can be converted to P₄O₆ and therefore contribute to process yield. These recovered phosphorus-containing species include unconverted phosphorus-containing species and/or may be provided by degradation products of P₄O₆. Rather than disposing of these compounds, their value as a source of phosphorus for P₄O₆ production is recovered by recycle to the reactor unit.

In accordance with the present invention it has been discovered that the manner of treatment and nature of the recycle stream recovered and returned to the reactor provides significant process benefits. Prior methods have included recycle of a slurry byproduct stream to the reactor unit. However, this has been observed to result in over-cooling of the reaction product within the reactor, which in turn lowers the yield during any single pass through the reactor and also prevents any significant recycle of reaction byproducts. Also, temperature control within the reactor unit using a slurry byproduct stream is not reliable due to significant clogging risks (e.g., of pumping mechanism) and may also lead to damage and even complete shut-down of the reactor. In addition, where a slurry byproduct stream is used additional energy requirements are imposed on the reactor. These additional energy requirements result in increased heat load on the reactor. Identifying suitable reactor materials and/or an insulated reactor that can withstand these conditions has proven costly, impractical, and/or cost-prohibitive. For example, commonly used materials such as aluminum oxide (Al₂O₃) and silicon carbide have been observed to suffer damage from overheating and/or corrosion caused by the reactants in methods employing slurry recycle.

Use of a vaporous recycle stream prepared in and recovered from a separate vaporization unit specifically selected for treatment of the recycle stream has been discovered to overcome these issues. Utilizing a vaporous recycle stream results in reduced variation in recycle flow rate, little, if any solid vaporization within the reactor unit and the problems associated therewith, and the negative effect(s) on reactor temperature associated with use of a solid byproduct stream. Overall, operation of the process allows for operation of the reactor unit on a more efficient basis in terms of temperature control. Therefore, reactors constructed of conventional materials known in the art (e.g., stainless steel) may be utilized for commercial-scale operations, typically along with direct and/or indirect cooling of the reactor contents as detailed elsewhere herein. Efficient recycle and reactor temperature control also provides improved product (P₄O₆) yield. It is also currently believed that utilizing a vaporous recycle stream allows for use of a reactor having a relatively low reactor volume and/or provides greater production of P₄O₆ on a unit reactor volume basis.

Reactor Unit

The processes of the present invention generally include the direct reaction of phosphorus and oxygen in a reactor unit designed for this purpose and at stoichiometric ratios. Phosphorus starting material (typically white phosphorus, P₄) can be introduced directly into the reactor unit (with or without prior vaporization). In certain embodiments, liquid phosphorus is utilized as a starting material, which is vaporized prior to its introduction into the reactor unit. Phosphorus starting material may also be provided by process streams generated elsewhere in processes of the present invention, including byproduct streams recovered during separation methods (optionally including vaporization of the byproduct stream between recovery and introduction into the reactor unit). In various preferred embodiments, a vaporized recycle stream is introduced into the reactor unit. In accordance with certain such embodiments, the vaporized recycle stream is the lone source of phosphorus introduced into the reactor unit.

Since the stoichiometric ratio of phosphorus:oxygen in P₄O₆ is 4:6, generally the molar ratio of phosphorus:oxygen present in the reactor unit is controlled to be near this value. Slight variations are permitted, however, with this ratio typically being from about 4:5.4 to about 4:6.6.

With reference to FIG. 1, phosphorus feed stream 1 and oxygen feed stream 5 are introduced into reactor unit 9. As indicated by dashed lines (and as detailed elsewhere herein), a separate phosphorus source is not required and the lone source of phosphorus for the reactor unit may be recovered elsewhere in the process and recycled to the reactor unit. It is to be understood that the conditions of the reactor depending on the proportion of phosphorus may be determined and controlled by either or both of these sources of phosphorus.

The direct reaction of phosphorus and oxygen is generally conducted in the presence of a flame within the reactor unit. Without cooling, the reactor mixture can reach excessive temperatures, which can result in the production of unwanted oxides of phosphorus (e.g., mixed P(III/V) oxides, phosphorus suboxides, and elemental phosphorus.

Given the highly exothermic nature of the reaction of phosphorus and oxygen, control of the temperature within the reactor unit and therefore the exit temperature of the reaction product recovered from the reactor unit are important aspects of the invention. Generally, the exit temperature of the intermediate reaction product stream as it is recovered from the reactor unit is at least about 1100K. Typically, the exit temperature of the product from the reactor unit is from about 1100 K to about 2200 K, or from about 1500K to about 2200K. Within these temperature ranges, the P₄O₆ product is relatively stable, thereby avoiding excessive loss in product yield by, for example degradation to the unwanted byproduct elemental phosphorus. It is currently believed that certain temperature conditions within the above-noted ranges are particularly useful for avoiding product decomposition, including those where the temperature is maintained below about 1800 K (e.g., from about 1500K to about 1800K or from about 1650K to about 1800K).

Providing the desired stoichiometric ratio of phosphorus and oxygen and controlling the temperature conditions within the reactor unit and the exit temperature of the product are dependent on one or more process variables, including phosphorus feed rate, oxygen feed rate, and the feed rate of any recycle stream introduced into the reactor. Generally in accordance with the present invention, any or each of these conditions may be adjusted in response to one of the specified conditions being outside its desired range of values, or in response to the composition of the intermediate reaction product stream recovered from the reactor unit.

Typically, phosphorus is introduced into the reactor unit at a rate of at least about 85 grams/hour, including at rates of from about 85 to about 500 grams/hour or from about 90 grams/hour to about 500 grams/hour.

Oxygen is typically fed to the reactor unit at a rate of at least about 70 grams/hour, including at rates of from about 70 to about 500 grams/hour or from about 80 to about 500 grams/hour.

Generally, where utilized, a vaporous recycle stream is introduced into the reactor unit at a rate of at least about 50 grams/hour, or from about 100 to about 500 grams/hour.

Where necessary to achieve the desired temperature conditions within the reactor and/or the desired exit temperature of the reactor product, the contents of the reactor unit and/or the reactor unit itself may be cooled.

In certain aspects, temperature control may be provided by direct cooling of the reactor contents. Materials suitable for direct cooling include recovered byproducts, reaction slurry recovered from any previous run, and P₄O₆ recovered from elsewhere in the process.

Separately, or along with direct cooling the reactor may also be cooled by indirect cooling. Indirect cooling of the reactor unit may be achieved by directly cooling the exterior of the reactor unit (e.g., by blowing cool air onto the exterior of the reactor unit). The reactor unit may also be cooled by surrounding the reactor unit with a bundle of heat exchange tubes for transfer of heat from the contents of the reactor unit to a heat transfer medium for removal of heat from the reactor unit. The selection of the heat transfer medium is not narrowly critical and may include those generally suitable in the art including, for example, air, water, and suitable oils.

Reaction of phosphorus and oxygen in the reactor unit provides a product, often referred to herein as an intermediate reaction product stream comprising P₂O₃ and one or more byproducts recovered from the reactor unit.

P₂O₃ generally constitutes at least about 60% by weight, at least about 70% by weight, or at least about 80% by weight of the intermediate reaction product stream. Typically, P₂O₃ constitutes from about 60 to about 90% by weight, from about 70 to about 90% by weight, or from about 80 to about 90% by weight of the intermediate reaction product stream.

Generally, the one or more byproducts of the intermediate reaction product stream comprise: (i) one or more oxides of phosphorus of the general formula P_(x)O_(y) where x is from 1-4 and y is from 1-10, and (ii) one or more other phosphorus species selected from the group consisting of P, P₂, P₃, P₄, and combinations thereof

Typically, the one or more byproducts of the intermediate reaction product stream comprise phosphorus (III) oxides, phosphorus (V) oxides, and phosphorus (III and V) oxides. These byproducts may be selected from the group consisting of P₄O₇, P₄O₈, P₄O₉, P₂O₅, and/or P₄O₁₀. Additionally, the one or more byproducts of the intermediate reaction product stream may comprise elemental phosphorus (P₄) and red phosphorus (P).

As noted, advantageously the processes of the present invention are suitable for P₄O₆ production on a commercial scale. It is currently believed that various features of the present invention provide advantageous yields, or payloads in terms of reactor volume as compared to other methods known in the art. Reactor volume is selected to provide the payload desired for the process of interest. The reactor may be constructed of any suitable material known in the art including, for example, stainless steel.

Quenching Unit

Again with reference to FIG. 1, the product of the reactor unit (intermediate reaction product stream) 12 is recovered from the reaction unit and introduced into quenching unit 15 along with quenching liquid 18. As shown in FIG. 1 by the dashed lines, the quenching liquid optionally may be a stream recovered from elsewhere in the process. As depicted in FIG. 1, the quenching liquid is from a product provided by a separation method (detailed elsewhere herein). However, it is to be understood that the quenching liquid can be provided by other product streams generated in the processes of the present invention and/or may also be a dedicated stream introduced into the process solely for use as the quenching liquid.

Quenching of the intermediate reaction product and lowering the temperature of this product stream is important as it serves to avoid undesired decomposition of the P₄O₆ product and therefore contributes to effective product yields and purities. Generally, the goal of the quenching step is to lower the temperature of the intermediate reaction product stream to below about 700K, or below about 500K. Typically, this cooling is conducted in a single step by contact with the quenching liquid. Generally the temperature of the quenching liquid is at least about 293K or from about 293K to about 423K.

The precise composition of the quenching liquid is not narrowly critical and in various embodiments is any inert liquid suitable to provide the desired cooling effect. In various embodiments, the quenching liquid does not have solubility in P₄O₆, and vice versa. In various embodiments, the quenching liquid comprises liquid P₄O₆ and may comprise liquid P₄O₆ recovered from a reaction product slurry provided as detailed elsewhere herein.

Contact of the intermediate reaction product stream with the quenching liquid within the quenching unit provides a reaction product slurry comprising liquid P₄O₆and one or more byproducts.

The reaction product slurry has a relatively high P₄O₆ content, typically of at least about 70% by weight, at least about 80% by weight, or at least about 90% by weight of the reaction product slurry.

The reaction product from the quenching unit is a slurry including a solids fraction and a liquid fraction. Typically, the liquid fraction of this slurry constitutes at least about 80% by weight, or at least about 90% by weight of the slurry. The slurry typically has a solids content of less than about 20% by weight, or less than about 10% by weight. Therefore, the liquid fraction typically constitutes at least about 80% by weight or at least about 90% by weight of the reaction product slurry.

The reaction product slurry contains one or more byproducts, including: (i) one or more higher oxides of phosphorus of the general formula P₄O_(y) where y is from 7-9, (ii) lower oxides of phosphorus (e.g., P₄O), and/or (iii) elemental phosphorus (P₄) and red phosphorus (P). At least a portion of the byproducts are solid while a portion of the byproducts are distributed through the liquid fraction of the slurry.

Overall, therefore, the process stream recovered from the quenching unit is generally in the form of a mixture or slurry of a relatively high moisture content along with a solids fraction generally constituted by one or more solid byproducts of the reaction of phosphorus and oxygen. As detailed elsewhere herein, byproducts are useful for recycle to the reactor unit to contribute to direct cooling of the contents of the reactor unit. Thus, various aspects of the present invention involve recovery from, or separation of the solid products from the reaction product slurry.

Separation Unit(s)

Again with reference to FIG. 1, reaction product slurry 21 is recovered from the quenching unit 15 and introduced into separation unit 24. Although shown singly in the schematic of FIG. 1, it is to be understood that a “separation unit” in accordance with the separation methods described herein may involve multiple unit operations or apparatus. Overall, however, the purpose of the use of a separator unit is providing at least two outputs: a byproduct stream 27 and a crude P₄O₆ product stream 30, as shown in FIG. 1.

A first step in separation is typically removal of a portion of the liquid phase of the reaction product slurry. The precise method for removal of a portion of the liquid phase at this stage is not narrowly critical and may be conducted, for example, by heating the reaction product slurry, including heating to a temperature of at least about 90° C. or at least about 100° C. or from about 100° C. to about 500° C.

Given its solids content and after having liquid removed therefrom the reaction product slurry may therefore be referred to herein as a thickened product slurry. The recovered liquid phase can be recycled back to the quenching unit and/or a portion may be sent to a distillation step (described elsewhere herein).

Generally, P₄O₆ constitutes at least about 80% by weight, at least about 90% by weight, or at least about 95% by weight of the thickened product slurry. The thickened product slurry typically has a moisture content of less than about 80% by weight or less than about 70% by weight. Concomitantly, the thickened product slurry has a solids content of at least about 20% by weight or at least about 30% by weight.

A fraction comprising liquid and solid components of the thickened product is recovered from the thickened product slurry. This fraction is shown as byproduct stream 27 in FIG. 1. A crude product stream comprising P₄O₆ (shown as 30 in FIG. 1) remains after recovery of the solids fraction from the thickened product slurry. The solids fraction may be recovered from the thickened product slurry in accordance with conventional solid-liquid separation apparatus known in the art including, for example, a hydrocyclone, a centrifuge, a filtration apparatus, or an evaporative apparatus.

In various other embodiments, a crude product stream is recovered from the thickened product slurry and the entire remaining slurry—the thickened product slurry, or thickened recycle stream is recycled to a vaporizer unit (detailed elsewhere herein).

As noted above, one output from the separation unit is a byproduct-containing stream, which is treated to provide a recycle stream (e.g., a vaporized recycle stream as detailed elsewhere herein) for returning to the reactor unit, as detailed elsewhere herein. Generally speaking, byproduct stream 27 may be recovered in the form of a slurry byproduct stream or in the form of a solid byproduct stream. The former case of a slurry byproduct stream typically contains a solid phase containing byproducts along with a liquid phase throughout which the solid phase is dispersed. In certain embodiments, a slurry byproduct stream may be further treated by removal of liquid therefrom to form a byproduct stream that is essentially a solids fraction having most or nearly all the liquid removed therefrom.

Therefore, in certain embodiments, from the thickened product slurry 21 is recovered a solids fraction 33, a crude product stream comprising P₄O₆ 30, and slurry byproduct stream 27. In various other embodiments, a solid byproduct stream is desired for further treatment and recycle to the reactor unit. In these embodiments, the slurry byproduct stream is dried to provide a solid byproducts stream.

Any solid byproduct stream generated typically has a moisture content of less than about 5% by weight, less than about 3% by weight, or less than about 1% by weight. Both a solid byproduct stream and a slurry byproduct stream may be treated in a vaporizer unit as detailed elsewhere herein, generally to provide a vaporized recycle stream for introduction back into the reactor unit.

Overall, therefore, operations within the broadly-defined “separation unit” can include: (i) removing liquid from the reaction product slurry to provide a thickened product slurry; and (ii) separating solid components of the thickened product slurry therefrom, thereby forming a slurry byproduct stream comprising the one or more solid byproducts and a crude product stream comprising P₄O₆. Such operations may also include: (i) removing liquid from the reaction product slurry to provide a thickened product slurry; (ii) separating solid components of the thickened product slurry therefrom, thereby forming a slurry byproduct stream comprising the one or more solid byproducts and a crude product stream comprising P₄O₆; and (iii) drying the slurry byproduct stream, thereby forming the one or more solid byproducts.

The crude product stream comprising P₄O₆ contains P₄O₆ and also typically contains P₄O₇ and P₄O₉. P₄O₆ typically constitutes at least about 80% by weight or at least about 90% by weight of the crude product stream. The crude product stream comprising P₄O₆ may also contain a liquid fraction.

Again with reference to FIG. 1, a second solids fraction may be recovered from the separation unit, optionally (dashed lines) shown as 33. This solids fraction may be separately recovered from the thickened product slurry itself or may be a portion of a slurry byproduct stream or a solids byproduct stream recovered as detailed elsewhere herein. If recovered, this solids fraction is treated as detailed elsewhere herein.

Vaporizer Unit

Generally, various processes of the present invention involve vaporizing, or treating in a vaporizer a byproduct stream recovered from the product of the quenching operation. This treatment provides a vaporized recycle stream generally comprising one or more phosphorus oxides (e.g., P₄O₁₀, or one or more phosphorus oxides of the general formula P_(x)O_(y)). The vaporized recycle stream is introduced into the reactor unit and may be combined with another source of phosphorus starting material or may be the lone source of phosphorus starting material introduced into the reactor unit. Again with reference to FIG. 1, byproduct stream 27 becomes vaporizer feed stream 36 that is introduced into vaporizer unit 39 to form vaporized recycle stream 42. Vaporizer feed steam may be in the form of a solid byproduct stream, or slurry byproduct stream with each situation detailed below.

Solid Byproducts

Overall, a solid byproduct stream recovered by separation operations as detailed elsewhere herein includes solid byproducts and a moisture fraction. Generally, the solid byproducts have a moisture content of less than about 30% by weight, less than about 20% by weight, or less than about 10% by weight. In certain embodiments, the solid byproducts have a moisture content of less than about 5% by weight, less than about 3% by weight, or less than about 1% by weight. The solid byproducts generally comprise: (i) one or more higher oxides of phosphorus of the general formula P₄O_(y) where y is from 7-9, (ii) lower oxides of phosphorus such as P₄O, and/or (iii) elemental phosphorus (P₄) and red phosphorus (P). Solid byproduct containing streams described herein may contain any or all of these byproducts.

Vaporization of the solid byproducts generally proceeds in the presence of an oxygen-containing gas and at elevated temperatures. Generally, the temperature within the vaporizer unit is at least about 773K. Often, the temperature within the vaporizer unit is at least about 1000K, or at least about 1100K and generally controlled at between 1200 K and 1770K. Typically, the temperature within the vaporizer unit is controlled at between 1200K and 1500K. Overall, the components of the vaporizer feed stream are vaporized at temperatures of greater than 1000K, greater than 1100K, or greater than 1200K.

Again with reference to FIG. 1, oxygen-containing gas 45 is introduced into the vaporizer unit. Suitable oxygen-containing gases include air and blends of oxygen and nitrogen. Where a blend of oxygen and nitrogen is employed, typically the amount of nitrogen is controlled to be a relatively minor portion of the gas stream to avoid over-cooling within the vaporizer unit. In various embodiments, only oxygen, or an oxygen-containing gas is introduced into the vaporizer unit along with the solid byproduct stream.

Vaporizing the solid byproduct stream by contact with an oxygen-containing gas in the vaporizing unit provides a vaporized recycle stream including P₄O₁₀. Other phosphorus oxides of the general formula P_(x)O_(y) may also be present in the vaporized recycle stream, but the predominant phosphorus oxide is P₄O₁₀. More specifically, in accordance with such embodiments, typically P₄O₁₀ constitutes at least about 40 weight % or at least about 50 weight % of the phosphorus oxides in a vaporized recycle stream where only an oxygen-containing gas is introduced into the vaporizer unit along with the solid byproduct stream.

It is currently believed that operating the vaporizer unit under certain conditions promotes a vaporized recycle stream where a substantial portion or nearly all of the phosphorus oxide species are constituted by P₄O₁₀. These conditions include a ratio of mass flow rates for the oxygen-containing gas and the one or more byproducts introduced into the vaporizer unit is from about 1:10 to about 10:1; and/or the temperature of the oxygen-containing gas introduced into the vaporizer unit of at least about 270K (e.g., from about 270K to about 500K, or from about 300K to about 500K); and/or the temperature of the one or more solid byproducts introduced into the vaporizer unit is at least about 270K (e.g., from about 270K to about 500K, or from about 300K to about 500K).

Under certain temperature conditions in the vaporizer unit, formation of the phosphorus oxide P₂O₅ results. To provide a vaporized recycle stream including P₂O₅ (optionally meeting the listed compositional limitations) the temperature within the vaporizer unit is controlled at from about 1200K to about 1500K.

An additional source of phosphorus may be introduced into the vaporizer unit along with the solid byproducts and oxygen-containing gas, shown (optionally by dashed lines) as 48 in FIG. 1. The additional phosphorus source (e.g., P₄) is generally believed to conduce formation of a broader complement of phosphorus oxides in the vaporized recycle stream, specifically one or more oxides of phosphorus of the general formula P_(x)O_(y) where x is from 2 to 4 and y is from 6-10.

For providing a vaporized recycle stream having a composition defined in such a manner, typically one or more of the following conditions are met: the ratio of mass flow rates for the oxygen-containing gas and the one or more byproducts introduced into the vaporizer unit is from about 1:10 to about 10:1; and/or the ratio of mass flow rates for the phosphorus (P₄) and the one or more byproducts introduced into the vaporizer unit is from about 1:10 to about 10:1; and/or the temperature of the oxygen-containing gas introduced into the vaporizer unit is at least about 270K (e.g., from about 270K to about 500K, or from about 300K to about 500K); and/or the temperature of the one or more byproducts introduced into the vaporizer unit is at least about 270K (e.g., from about 270K to about 500K, or from about 300K to about 375K).

The temperature of the vaporized recycle stream typically is at least about 1000K, or at least about 1100K. In various embodiments, the temperature of the vaporized recycle stream is from about 1000K to about 2000K, or from about 1200K to about 2000K. Although generally vaporous in nature, the vaporized recycle stream may contain a minor solids fraction of less than about 5 weight %.

Again with reference to FIG. 1, the vaporized recycle stream 42 is introduced into the reactor unit 9. The vaporized recycle stream may be the lone source of phosphorus reacted with oxygen in the reactor unit. Therefore, the phosphorus starting material 1 shown in FIG. 1 is optional (indicated by dashed lines) and in certain embodiments not included.

As detailed elsewhere herein, control of the conditions within the reactor unit is important in order to provide the reaction product with an exit temperature that avoids substantial decomposition of the desired product. Another purpose of addition of the vaporized recycle stream into the reactor unit therefore is direct cooling of the contents of the reactor unit. Therefore, in accordance with the present invention, the temperature within the reactor unit may be controlled by direct cooling of the reactor contents, with direct cooling comprising introducing a vaporized recycle stream into the reactor unit.

Slurry Byproduct

Further in accordance with the present invention, and with reference to FIG. 1, byproduct stream 27 may be a slurry that is introduced into the vaporizer unit to provide a vaporized recycle stream that is introduced into the reactor unit. Typically, the slurry byproduct stream includes a liquid fraction that constitutes from about 5% by weight to about 50% by weight of the slurry byproduct stream.

The slurry byproduct stream typically contains a significant fraction of solid byproducts (i.e., (i) one or more higher oxides of phosphorus of the general formula P₄O_(y) where y is from 7-10, (ii) lower oxides of phosphorus such as P₄O, and/or (iii) elemental phosphorus (P₄) and red phosphorus (P)).

An oxygen-containing gas (and optionally an additional source of phosphorus (e.g., P₄)) is introduced into the vaporizer unit along with the slurry byproduct.

Where a slurry byproduct stream is recovered and sent to a vaporizer unit to provide vaporized recycle stream for use in the reactor unit, one or more conditions of operation of the vaporizer unit may be controlled in order to provide a vaporized recycle stream having one or more desirable features. Typically, the ratio of mass flow rates for the oxygen-containing gas and the slurry byproduct introduced into the vaporizer unit is from about 1:10 to about 10:1; and/or the ratio of mass flow rates for the phosphorus (P₄) and the slurry byproduct introduced into the vaporizer unit is from about 1:10 to about 10:1; and/or the temperature of the oxygen-containing gas introduced into the vaporizer unit is at least about 270K (e.g., from about 270K to about 500K, or from about 300K to about 500K); and/or the temperature of the one or more byproducts introduced into the vaporizer unit is at least about 270K (e.g., from about 270K to about 500K, or from about 300K to about 375).

A vaporized recycle stream provided by a slurry byproduct stream introduced into the vaporizer typically contains phosphorus oxides of the general formula P_(x)O_(y), where x is from 1-4 (e.g., 2-4) and y is from 1-10 (e.g., 6-10). The temperature of such a vaporized recycle stream typically is from about 750K to about 1700K. Although generally vaporous in nature, the vaporized recycle stream may contain a minor solids fraction constituting less than about 5 weight %.

One purpose of introduction of such a vaporized recycle stream is to provide a source of phosphorus for reaction with oxygen within the reactor unit, and the vaporized recycle stream may be the lone source of phosphorus reacted with oxygen in the reactor unit.

The purpose of the vaporized recycle stream may also be direct cooling of the reactor contents to provide a product recovered from the reactor unit at a desired exit temperature.

Regardless of the precise nature of the byproduct stream introduced into the vaporizer unit, reaction therein is exothermic. Typically, the vaporizer unit may be externally cooled.

Solid Byproducts Recycle to Reactor Unit

In certain embodiments of the present invention, a solid byproduct stream is recovered from a separator unit and recycled to the reactor unit without treatment in a vaporizer unit. With reference to FIG. 2, oxygen-containing gas 101 and phosphorus source 104 are introduced into reactor unit 107 to form intermediate reaction product stream 110. This product stream is introduced into quenching unit 114 and contacted with quenching liquid 116 to form a reaction product slurry 118 comprising P₄O₆ and one or more solid byproducts. The reaction product slurry is introduced into the separator unit 121 for recovery of a solid byproduct recycle stream 127 for recycle to reactor unit 107. The solid byproduct stream is recovered from the reaction product by a suitable method known in the art.

Recycle of the solid byproducts to the reactor unit provides a source of phosphorus for reaction within the reactor unit and also provides some direct cooling of the reactor contents. The direct cooling of the reactor contents by introduction of the solid byproducts may not be sufficient to control the temperature such that a product of the desired exit temperature for release from the reactor unit is provided. In accordance with the present invention it has been discovered that the temperature conditions within the reactor unit may be controlled by further employing external cooling of the reactor unit.

Advantageously in accordance with the present invention it has been discovered that combining direct cooling of the reactor unit contents by introducing solid byproducts thereto along with external cooling of the reactor unit allows for_improved yield, decreased decomposition, and better temperature control within the reactor unit. In addition, conventional reactor materials could be used for construction as excessive heating is not caused due to combined better control of external cooling and controlled internal cooling

Typically, the solid byproducts recovered from the reaction product slurry comprise: (i) one or more oxides of phosphorus of the general formula P₄O_(y) where y is from 7-10, (ii) lower oxides of phosphorus such as P₄O, and/or (iii) elemental phosphorus (P₄) and red phosphorus (P).

Typically, the solid byproducts recovered from the reaction product slurry have a moisture content of less than about 30% by weight, less than about 20% by weight, less than about 10% by weight, or less than about 5% by weight.

Aside and apart from any temperature control aspect, typically the rate of addition of the one or more solid byproducts into the reactor unit is controlled to maintain the molar ratio of P:O within the reactor unit at from about 4:5.4 to about 4:6.6.

Where the solid byproducts are not the lone source of phosphorus introduced into the reactor unit, generally the relative proportions of solid byproducts, other phosphorus source, and oxygen introduced into the reactor unit may be controlled in order to provide the desired conditions within the reactor unit. Typically, the ratio of the mass flow rates of the one or more solid byproducts and phosphorus introduced into the reactor unit is at least about 0.2:1 or from about 0.3:1 to about 1:1. The ratio of the mass flow rates of the one or more solid byproducts and oxygen introduced into the reactor unit is at least about 0.25:1 or from about 0.4:1 to about 1:1.4.

Phosphorus (III) Oxide Product Recovery and Purification

Again with reference to FIG. 1, a crude product stream comprising P₄O₆(crude product stream) 30 is recovered from the separator unit and subjected to one or more purification methods to provide a purified final product. The crude product stream, obtained after recovery of a byproduct stream (e.g., a solid byproduct or slurry byproduct stream) from an upstream phosphorus (III) oxide containing stream includes a liquid fraction along with a solids fraction. The crude product stream therefore comprises liquid P₄O₆. Generally speaking, P₄O₆ constitutes at least about 80% by weight or at least about 90% by weight of the crude product stream. The crude product stream may also have a solids fraction including one or more solid byproducts. Since the byproduct and solids fractions include minimal P₄O₆, generally speaking the crude product stream is enriched in P₄O₆ content as compared to the upstream process streams by virtue of removal of fractions of minimal, if any P₄O₆ content (e.g., the solid and/or slurry byproduct stream recovered and subjected to one or more operations as detailed elsewhere herein).

For recovery of a purified P₄O₆ product, the crude product stream is purified by one or more operations. In various embodiments, the crude product stream is distilled. Generally in accordance with such embodiments, and again with reference to FIG. 1, the crude product stream is introduced into distillation zone 33.

The crude product stream, generally in the form of a liquid phase containing dissolved P₄O₆ and a minor impurity fraction is introduced into the distillation zone and subjected to elevated temperature conditions to form an overheads fraction and a bottoms fraction. The overheads fraction includes P₄O₆ and the solids fraction comprises solid byproducts. The overheads fraction comprising P₄O₆ is condensed to form a liquid P₄O₆ product. Suitable distillation methods include those generally known in the art.

The final, liquid P₄O₆ product of the present invention may be characterized by any or all of the following features: (i) a yield of at least 90%, at least 95%, or at least 99% based on the total amount of phosphorus introduced into the reactor unit; and/or (ii) a P₄O₆ purity of at least about 90%, at least 95%, or at least 99%; and/or (iii) an elemental phosphorus (P₄) content of no more than about 10 wt % or no more than about 5 wt %; and/or (iv) as essentially free of elemental phosphorus (P₄).

The bottoms fraction may be recovered and disposed of or may be re-introduced at one or more points in the process in the hope of recovering value from any phosphorus-containing species that may be present in the fraction. For example, in certain embodiments, a portion of the bottoms fraction 39 comprising solid byproducts may be combined with the reaction product slurry prior to its introduction into the separation unit 24.

Additionally or alternatively, at least a portion of the bottoms fraction comprising solid byproducts may be combined with solid byproducts recovered from the thickened product slurry (not shown in FIG. 1) to form a combined solid byproducts stream. At least a portion of the combined solid byproducts stream thus formed may be introduced into the vaporizer unit.

Again with reference to FIG. 1, in certain embodiments a portion of the crude product stream 50 is returned to the quenching unit 15.

Alternative Phosphorus Oxide and Phosphoric Acid Production

As noted elsewhere herein, the present invention is further directed to processes for the preparation of phosphorus oxides other than P₄O₆ including, for example, P₂O₅. Certain processes of the present invention also include preparation of phosphoric acid. Generally in accordance with such embodiments of the present invention, the starting material is a solids-containing byproduct stream recovered during separation of a crude product stream and solid byproducts. Again with reference to FIG. 1, the starting material 33 is treated as discussed herein with reference to FIG. 3 (phosphoric acid) and FIG. 4 (P₂O₅). Each of these processes may be combined with one or more of the processes detailed herein, including those described in FIGS. 1 and 2.

Generally in accordance with the present invention, preparation of phosphoric acid involves vaporizing a solid byproduct stream, followed by hydrating of the vaporized stream to form a liquid product comprising phosphoric acid.

With reference to FIG. 3, the solid stream 333 is combined with an oxygen-containing gas 336 in vaporizer 339.

The ratio of mass flow rates for the oxygen-containing gas and the solid stream introduced into the vaporizer unit is from about 1:10 to about 10:1; and/or the temperature of the oxygen-containing gas introduced into the vaporizer unit is at least about 270K (e.g., from about 270K to about 500K, or from about 300K to about 500K); and/or the temperature of the solid stream introduced into the vaporizer unit is at least about 270K (e.g., from about 270K to about 500K, or from about 300K to about 500K).

Generally, the temperature within the vaporizer unit is at least about 773K. Often, the temperature within the vaporizer unit is at least about 1000K, or at least about 1100K. Overall, the temperature within the vaporizer unit typically is controlled at between 1200 K and 1770K. Typically, the temperature within the vaporizer unit is is controlled at between 1200 K and 1500 K. Typically, the components of the vaporizer feed stream are vaporized at temperatures of greater than 1000K, greater than 1100K, or greater than 1200K.

From the vaporizer unit 339 is recovered a vapor product stream 342 containing P₂O₅ and/or P₄O₁₀.

The vapor product stream 342 is then introduced into a hydrator 345, wherein the vapor is contacted with water to form phosphoric acid.

Generally, the ratio of the mass flow rates for the vapor product stream and water present in the hydrator is from about 1:10 to about 10:1.

With reference to FIG. 4, the solid product stream 433 is combined with oxygen 436 in vaporizer unit 439 to provide a vapor product stream 442. The conditions within the vaporizer unit and the composition of vapor product stream 442 are generally the same as those set forth above.

The vapor product stream 442 is introduced into a condenser 445 to provide product stream 448 comprising P₂O₅.

Preparation of Phospho-Herbicides

As previously noted, certain embodiments of the present invention involve use of phosphorus (III) oxides (e.g., P₄O₆) and other products obtained from the processes of the present invention (e.g., phosphorous acid) in processes for the preparation of phospho-herbicides such N-(phosphonomethyl)glycine (glyphosate) and precursors thereof (e.g., N-(phosphonomethyl)iminodiacetic acid (PMIDA)).

Processes for making PMIDA are known in the art and include those in which an alkali metal salt of iminodiacetic acid (IDA), a strong mineral acid, and a source of phosphorous acid are reacted. The disodium salt of IDA (DSIDA) is preferred. Suitable strong mineral acids include sulfuric, hydrobromic, hydroiodic and hydrochloric with hydrochoric generally preferred. In conventional methods, phosphorous acid can be added to the reaction medium or generated in situ by the hydrolysis of PCl₃. In such methods, PCl₃ is hydrolyzed to phosphorus acid in the DSIDA solution. HCl, which results from hydrolysis of phosphorous trichloride, acidifies the DSIDA to afford the hydrochloride salt and NaCl. Water vapor and a fraction of the HCl may be evolved from the reaction mixture and recovered in a hydrolysis reactor condenser. Optionally, a fraction of HCl driven from the reaction may be recycled to a subsequent batch. The IDA hydrochloride salt and NaCl are both substantially insoluble and form a slurry in an aqueous solution which is saturated with HCl. In a second step, the hydrolyzate slurry containing the strong acid salt of iminodiacetic acid, sodium chloride, hydrochloric acid and phosphorous acid is transferred from the hydrolyzer to a phosphonomethylation (PM) reactor. In the PM reactor, the slurry is combined with a source of formaldehyde to produce a PM reaction mixture containing PMIDA.

The present invention includes methods where P₄O₆ prepared in accordance with any of the methods described herein is utilized for the in situ preparation of phosphorous acid, thus avoiding the issues associated with PCl₃ detailed elsewhere herein. Such methods generally proceed as described above with the PCl₃ replaced by the P₄O₆.

The present invention is further directed to methods where P₄O₆ prepared or recovered as described herein is utilized in a method for preparing PMIDA in a method that does not require the use of a strong mineral acid (e.g., hydrochloric acid). In such methods, P₄O₆ is hydrolyzed to form phosphorous acid, which is then reacted with formaldehyde and IDA to form PMIDA. In addition to avoiding the use of PCl₃ and the issues associated therewith, these methods therefore further avoid the issues associated with the use of hydrochloric, including the generation of chloride byproducts.

The present invention is further directed to methods where PMIDA prepared as described herein is converted to N-(phosphonomethyl)glycine in accordance with methods generally known in the art.

Having described the invention in detail, it will be apparent that modifications and variations are possible without departing from the scope of the invention defined in the appended claims.

EXAMPLES

The following non-limiting examples are provided to further illustrate the present invention.

Example 1 P₄O₆ Process with Byproducts Vaporization

A stream (99 g/h) of liquid elemental phosphorus P₄(l) is pumped from a phosphorus storage tank (maintained at a temperature of approximately 323K) into a phosphorus evaporator (a tube furnace maintained at around 773K) and converted into a vaporous elemental phosphorus P₄(g) stream. The vaporous elemental phosphorus stream is injected into a vaporizer (an externally cooled stainless steel chamber), and reacted exothermically with a stream of oxygen gas (O₂) (77 g/h) that is also injected into the vaporizer to form a vaporous mixture of phosphorus oxides.

Concurrently, a stream of solid byproducts obtained from previous experiments (176 g/h) is fed into a vaporizer and vaporized by the reaction heat of P₄+O₂ into a separate vaporous mixture of various phosphorus oxides.

The vaporous mixtures of phosphorus oxides prepared from solid byproducts are injected into a reactor (an externally cooled or externally plus internally cooled stainless steel chamber) along with the resultant stream of vaporous mixture of phosphorus oxides prepared from elemental phosphorus along with a stream of oxygen gas (O₂) (230 g/h) and another stream of vaporous phosphorus P₄(g) (297 g/h) (generated from another phosphorus evaporator) are injected into a reactor, where they react to form a hot reaction product stream.

The heat removal from the reactor is controlled by the external cooling or external cooling plus internal cooling to ensure that the exit temperature of the hot reaction product stream is maintained at around 1710K so that the dominant species in the hot reaction product is the desired phosphorus trioxide P₂O₃(g).

Upon exiting the reactor, the hot reaction product stream is quenched in a quench unit by mixing it with a quench fluid. The quench liquid is a stream of liquid P₄O₆(l) (44,400 g/h) obtained from previous experiments.

The quenched product and the quench fluid are collected as a mixture (slurry) of liquid P₄O₆(l) and solid byproducts at the bottom the quench unit. With a hydrocyclone, the slurry is divided into two streams, one is a stream of thickened slurry and the other is a stream of clarified crude P₄O₆ product.

With a filtration unit or a centrifuge, the solid-liquid separation of the thickened slurry leads to a stream of solid byproducts and a stream of liquid crude P₄O₆ that contains some soluble byproducts.

The liquid crude P₄O₆ stream is purified using an evaporative distillation unit to provide 704 g/h purified product P₄O₆, while the soluble byproducts is precipitated from crude P₄O₆ to form solid distillation residue at the bottom of the distillation unit.

The purified product P₄O₆ has a purity of greater than 99 weight %. The P₄O₆ yield on P₄ introduced into the reactor unit is greater than 99%.

Example 2 P₄O₆ Process with Conversion of P_(x)O_(y) to H₃PO₄ or P₂O₅

A stream of liquid elemental phosphorus P₄(l) (500 g/h) is pumped from a phosphorus storage tank (maintained at a temperature of approximately 323K) into a phosphorus evaporator (a tube furnace maintained at around 773K) and converted into vaporous elemental phosphorus P₄(g). The P₄(g) stream and a stream of oxygen gas (O₂) (387 g/h) are injected into a reactor (an externally cooled or externally plus internally cooled stainless steel chamber), where they react into a stream of hot reaction product. The heat removal from the reactor is controlled by the external cooling or external plus internal cooling to ensure that the exit temperature of the hot reaction product stream is maintained at around 1710K so that the dominant species in the hot reaction product is the desired phosphorus trioxide P₂O₃(g).

Upon exiting from the reactor, the hot reaction product stream is quenched in a quench unit by mixing it with a quench fluid. The quench fluid is a stream of liquid P₄O₆(l) (44,400 g/h) obtained from previous experiments.

The quenched product and the quench fluid are collected as a mixture (slurry) of liquid P₄O₆(1) and solid byproducts at the bottom the quench unit. With a hydrocyclone, the slurry is divided into two streams, one is a stream of thickened slurry and the other is a stream of clarified crude P₄O₆.

With a filtration unit or a centrifuge, the solid-liquid separation of the thickened slurry leads to a stream of solid byproducts and a stream of liquid crude P₄O₆ that contains some soluble byproducts.

The liquid crude P₄O₆ stream is purified by an evaporative distillation unit to provide 710 g/h purified product P₄O₆, while the soluble byproducts is precipitated from crude P₄O₆ to form solid distillation residue at the bottom of the distillation unit.

The solid byproducts obtained in filtration/centrifuge and solid distillation residue are mixed together to form a stream of 177 g/h solid byproducts. This combined solid byproducts stream is fed into an oxidative vaporizer unit (an externally cooled stainless steel chamber), where the solid byproducts stream is oxidized exothermically by contact with a stream of at least 52 g/h oxygen gas (O₂) injected into the oxidation vaporizer, and converted into a vaporous byproduct stream containing phosphorus pentoxide (P₄O₁₀(g) and/or P₂O₅(g)).

The vaporous phosphorus pentoxide (P₄O₁₀(g), and/or P₂O₅(g)) is absorbed into a stream of dilute phosphoric acid H₃PO₄ and converted into concentrated phosphoric acid.

The purified P₄O₆ product has a purity of greater than 99 weight %. The impurity content of H₃PO₄ is less than 0.5%. The total yield on P₄ introduced into the reactor unit is >99%.

Example 3 P₄O₆ Process with Solid Byproducts Recycle

A stream of liquid elemental phosphorus P₄(l) (396 g/h) is pumped from a phosphorus storage tank (maintained at a temperature of approximately 323K) into a phosphorus evaporator (a tube furnace maintained at around 773K) and converted into vaporous elemental phosphorus P₄(g). The resultant P₄(g) stream, a stream of solid byproducts (obtained from previous experiments) (176 g/h) and a stream of oxygen gas (O₂) (384 g/h) are fed into a reactor (an externally cooled or externally plus internally cooled stainless steel chamber), where they react to form a stream of hot reaction product.

The heat removal from the reactor is controlled by the external cooling or external plus internal cooling to ensure that the exit temperature of the hot reaction product stream is maintained at around 1710K so that the dominant species in the hot reaction product is the desired phosphorus trioxide P₂O₃(g).

Upon exiting from the reactor, the hot reaction product stream is quenched in a quench unit by mixing it with a quench fluid, a stream of liquid P₄O₆(l) (44,400 g/h) obtained from previous experiments.

The quenched product and the quench fluid are collected as a mixture (slurry) of liquid P₄O₆(l) and solid byproducts at the bottom of the quench unit. With a hydrocyclone, the slurry is divided into two streams, one is a stream of thickened slurry and the other is a stream of clarified crude P₄O₆.

With a filtration unit or a centrifuge, the solid-liquid separation of the thickened slurry leads to a stream of solid byproducts and a stream of liquid crude P₄O₆ that contains some soluble byproducts.

The liquid crude P₄O₆ stream is purified by using evaporative distillation unit to provide 704 g/h purified P₄O₆ product, while the soluble byproducts are precipitated from the crude P₄O₆ to form solid distillation residue at the bottom of the distillation unit.

The purified product P₄O₆ has a purity of greater than 99 weight %. The P₄O₆ yield on P₄ introduced into the reactor unit is greater than 99%.

Example 4 P₄O₆ Process with Oxidation-Vaporization Step

A stream of liquid elemental phosphorus P₄(l) (400 g/h) is pumped from a phosphorus storage tank (maintained at a temperature of approximately 323K) into a phosphorus evaporator (a tube furnace maintained at around 773K) and converted into vaporous elemental phosphorus P₄(g).

Concurrently, a stream of 177 g/h solid byproducts obtained from previous experiments is fed into an oxidation vaporizer (an externally cooled stainless steel chamber), oxidized exothermically by a stream of oxygen gas O₂ (at least 52 g/h) injected into the oxidation vaporizer, and converted into vaporous phosphorus pentoxide (P₄O₁₀(g), and/or P₂O₅(g)). (At startup, when solid byproducts are not available for recycle, purchased red phosphorus or the mixture of purchased red phosphorus and purchased P₂O₅ may be optionally used in place of solid byproducts.)

The resultant P₄(g) stream and phosphorus pentoxide stream along with a stream of oxygen gas O₂ (258 g/h) are injected into a reactor (an externally cooled or externally plus internally cooled stainless steel chamber), where they react into a stream of hot reaction product. The heat removal from the reactor is controlled by the external cooling or external plus internal cooling to ensure that the exit temperature of the hot reaction product stream is maintained at around 1710K so that the dominant species in the hot reaction product is the desired phosphorus trioxide P₂O₃(g).

Upon exiting from the reactor, the hot reaction product stream is quenched in a quench unit by mixing it with a quench fluid and a stream of liquid P₄O₆(l) (44,400 g/h) obtained from previous experiments.

The quenched product and the quench fluid are collected as a mixture (slurry) of liquid P₄O₆(l) and solid byproducts at the bottom the quench unit. With a hydrocyclone, the slurry is divided into two streams, one is a stream of thickened slurry and the other is a stream of clarified crude P₄O₆.

With a filtration unit or a centrifuge, the solid-liquid separation of the thickened slurry leads to a stream of solid byproducts and a stream of liquid crude P₄O₆ that contains some soluble byproducts.

The liquid crude P₄O₆ stream is purified by an evaporative distillation unit to get 710 g/h purified product P₄O₆, while the soluble byproducts is precipitated from crude P₄O₆ to form solid distillation residue at the bottom of the distillation unit.

The purified product P₄O₆ has a purity of greater than 99 weight %. The P₄O₆ yield on P₄ introduced into the reactor unit is greater than 99%.

When introducing elements of the present invention or the preferred embodiments(s) thereof, the articles “a”, “an”, “the” and “said” are intended to mean that there are one or more of the elements. The terms “comprising”, “including” and “having” are intended to be inclusive and mean that there may be additional elements other than the listed elements.

In view of the above, it will be seen that the several objects of the invention are achieved and other advantageous results attained.

As various changes could be made in the above without departing from the scope of the invention, it is intended that all matter contained in the above description and shown in the accompanying drawings shall be interpreted as illustrative and not in a limiting sense. 

1. A process for the manufacture of phosphoric acid (H₃PO₄), the process comprising: reacting phosphorus with oxygen in a reactor unit, thereby forming an intermediate reaction product comprising P₂O₃ and one or more byproducts; in a quenching unit, quenching the intermediate reaction product by contacting with a quenching liquid, thereby forming a reaction product slurry comprising liquid P₄O₆ and one or more byproducts; separating liquid P₄O₆ from the reaction product slurry, thereby forming a crude product stream comprising liquid P₄O₆ and a byproduct stream comprising phosphorus (III) phosphorus (V) and/or phosphorus (III and V) oxides; introducing the byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the byproduct stream to produce a vapor product stream comprising P₂O₅ and/or P₄O₁₀; and contacting the vapor product stream with water, thereby forming a liquid product stream comprising H₃PO₄.
 2. A process for the manufacture of phosphorus pentoxide (P₂O₅), the process comprising: reacting phosphorus with oxygen in a reactor unit, thereby forming an intermediate reaction product comprising P₂O₃ and one or more byproducts; in a quenching unit, quenching the intermediate reaction product by contacting with a quenching liquid, thereby forming a reaction product slurry comprising liquid P₄O₆ and one or more byproducts; separating liquid P₄O₆ from the reaction product slurry, thereby forming a crude product stream comprising liquid P₄O₆ and a byproduct stream comprising phosphorus (III), phosphorus (V) and/or phosphorus (III and V) oxides; introducing the byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the byproduct stream to produce a vapor product stream comprising P₂O₅ and/or P₄O₁₀; and condensing the vapor product stream, thereby forming a product stream comprising solid P₂O₅.
 3. The process as set forth in claim 2, the process further comprising: separating the reaction product slurry into a crude liquid P₄O₆ stream and a thickened product slurry; and introducing the crude liquid P₄O₆ stream into the quenching unit.
 4. The process as set forth in claim 1, wherein the reaction product slurry is separated by a hydrocyclone, a centrifuge, filtration apparatus, or an evaporative apparatus.
 5. The process as set forth in claim 2, wherein the liquid P₄O₆ is separated from the thickened product slurry by solid-liquid separation method selected from the group consisting of centrifugation, filtration, hydrocyclone, or evaporation.
 6. The process as set forth in claim 1, the process further comprising: distilling the crude product stream comprising liquid P₄O₆ within a distillation zone, thereby forming an overheads fraction and a bottoms fraction, the overheads fraction comprising P₄O₆ and the bottoms fraction comprising one or more byproducts; and condensing the overheads fraction to form a liquid P₄O₆ product.
 7. The process as set forth in claim 6, the process further comprising: combining the bottoms fraction comprising one or more byproducts and the reaction product slurry; and separating liquid P₄O₆ from the combined slurry, thereby forming a crude product stream comprising liquid P₄O₆ and a byproduct stream comprising one or more byproducts; and in a vaporization unit, vaporizing the byproducts stream to form a recovered byproducts stream comprising P₄O₁₀, P₂O₅, or a mixture thereof; and absorbing the recovered byproducts stream in an aqueous medium comprising phosphoric acid, thereby forming a concentrated phosphoric acid stream.
 8. A process for the manufacture of phosphorus (III) oxide, the process comprising: in a reactor unit, reacting phosphorus with oxygen, thereby forming an intermediate reaction product stream comprising P₂O₃ and one or more byproducts; in a quenching unit, quenching the intermediate reaction product stream by contacting with a quenching liquid, thereby forming a reaction product slurry comprising P₄O₆ and one or more byproducts; recovering a first byproduct stream from the reaction product slurry; introducing an oxygen-containing gas along with the first byproduct stream into a vaporizer unit, wherein the components of the first byproduct stream are vaporized to form a vaporized recycle stream comprising P₂O₅ and/or P₄O₁₀; and introducing at least a portion of the vaporized recycle stream into the reactor unit.
 9. The process of claim 8, the process further comprising: recovering a second byproduct stream from the reaction product slurry, the second byproduct stream comprising phosphorus (III), phosphorus (V) and/or phosphorus (III and V) oxides; introducing the second byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the second byproduct stream to produce a vapor product stream comprising P₂O₅ and/or P₄O₁₀; and contacting the vapor product stream with water, thereby forming a liquid product stream comprising H₃PO₄.
 10. The process of claim 8, the process further comprising: recovering a second byproduct stream from the reaction product slurry, the second byproduct stream comprising phosphorus (III), phosphorus (V) and/or phosphorus (III and V) oxides; introducing the second byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the second byproduct stream to produce a vapor product stream comprising P₂O₅ and/or P₄O₁₀; and condensing the vapor product stream with water, thereby forming a product stream comprising solid P₂O₅.
 11. A process for the manufacture of phosphorus (III) oxide, the process comprising: in a reactor unit, reacting phosphorus with oxygen, thereby forming an intermediate reaction product stream comprising P₂O₃ and one or more byproducts; in a quenching unit, quenching the intermediate reaction product stream by contacting with a quenching liquid, thereby forming a reaction product slurry comprising P₄O₆ and one or more byproducts; recovering a first byproduct stream from the reaction product slurry; introducing an oxygen-containing gas, phosphorus (P₄), and the first byproduct stream into a vaporizer unit, wherein the components of the first byproduct stream are vaporized to form a vaporized recycle stream comprising one or more oxides of phosphorus of the general formula P_(x)O_(y) where x is from 1-4, y is from 1-10; and introducing at least a portion of the vaporized recycle stream into the reactor unit.
 12. The process of claim 11, the process further comprising: recovering a second byproduct stream from the reaction product slurry, the second byproduct stream comprising phosphorus (III), phosphorus (V) and/or phosphorus (III and V) oxides; introducing the second byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the second byproduct stream to produce a vapor product stream comprising P₂O₅ and/or P₄O₁₀; and contacting the vapor product stream with water, thereby forming a liquid product stream comprising H₃PO₄.
 13. The process of claim 11, the process further comprising: recovering a second byproduct stream from the reaction product slurry, the second byproduct stream comprising phosphorus (III), phosphorus (V) and/or phosphorus (III and V) oxides; introducing the second byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the second byproduct stream to produce a vapor product stream comprising P₂O₅ and/or P₄O₁₀; and condensing the vapor product stream with water, thereby forming a product stream comprising solid P₂O₅.
 14. The process of claim 11, wherein the vaporized recycle stream is the lone source of phosphorus reacted with oxygen in the reactor unit.
 15. The process of claim 14, the process further comprising: recovering a second byproduct stream from the reaction product slurry, the second byproduct stream comprising phosphorus (III), phosphorus (V) and/or phosphorus (III and V) oxides; introducing the second byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the second byproduct stream to produce a vapor product stream comprising P₂O₅ and/or P₄O₁₀; and contacting the vapor product stream with water, thereby forming a liquid product stream comprising H₃PO₄.
 16. The process of claim 14, the process further comprising: recovering a second byproduct stream from the reaction product slurry, the second byproduct stream comprising phosphorus (III), phosphorus (V) and/or phosphorus (III and V) oxides; introducing the second byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the second byproduct stream to produce a vapor product stream comprising P₂O₅ and/or P₄O₁₀; and condensing the vapor product stream with water, thereby forming a product stream comprising solid P₂O₅.
 17. A process for the manufacture of phosphorus (III) oxide, the process comprising: in a reactor unit, reacting phosphorus with oxygen, thereby forming an intermediate reaction product stream comprising P₂O₃ and one or more byproducts; in a quenching unit, quenching the intermediate reaction product stream by contacting with a quenching liquid, thereby forming a reaction product slurry comprising liquid P₄O₆ and one or more byproducts; separating solid components of the reaction product slurry therefrom, thereby forming a first byproduct stream comprising the one or more solid byproducts; introducing at least a portion of the first byproduct stream into a vaporizer unit; recovering a second byproduct stream from the reaction product slurry, the second byproduct stream comprising phosphorus (III), phosphorus (V) and/or phosphorus (III and V) oxides; introducing the second byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the second byproduct stream to produce a vapor product stream comprising P₂O₅ and/or P₄O₁₀; and contacting the vapor product stream with water, thereby forming a liquid product stream comprising H₃PO₄; or condensing the vapor product stream with water, thereby forming a product stream comprising solid P₂O₅.
 18. A process for the manufacture of phosphorus (III) oxide, the process comprising: in a reactor unit, reacting phosphorus with oxygen, thereby forming an intermediate reaction product stream comprising P₂O₃ and one or more byproducts; in a quenching unit, quenching the intermediate reaction product stream by contacting with a quenching liquid, thereby forming a reaction product slurry comprising liquid P₄O₆ and one or more solid byproducts; recovering a first byproduct stream comprising the one or more solid byproducts from the reaction product slurry; introducing the one or more solid byproducts into the reactor unit for direct cooling of the contents of the reactor unit, and wherein the temperature within the reactor unit is controlled by external cooling of the reactor unit; recovering a second byproduct stream from the reaction product slurry, the second byproduct stream comprising phosphorus (III), phosphorus (V) and/or phosphorus (III and V) oxides; introducing the second byproduct stream and oxygen into a vaporizer unit, thereby oxidizing phosphorus oxides present in the second byproduct stream to produce a vapor product stream comprising P₂O₅ and/or P₄O₁₀; and contacting the vapor product stream with water, thereby forming a liquid product stream comprising H₃PO₄; or condensing the vapor product stream with water, thereby forming a product stream comprising solid P₂O₅. 